EN 10083-2:98 Standard
W.NR.: 1.0402/C22
Non-Alloy High Grade Steel
Heat analysis according to the EN 10083-2: 98 standard
| C % | Si % | Mn % | P % | S % | Cr % | Ni % | Mo % | Cr+Mo+Ni % | |
| From | 0,17 | – | 0,40 | – | – | – | – | – | – |
| To | 0,24 | 0,40 | 0,70 | 0,045 | 0,045 | 0,40 | 0,40 | 0,10 | 0,63 |
According to the UNI 10233-3 standard
| Thickness mm | Cold Drawn | ||
| ( +C ) | |||
| Rp0,2 minimum | Rm minimum | A5 % | |
| (MPa) | (MPa) | minimum | |
| ≤5 | 450,00 | 570,00 | 5,00 |
| >5≤10 | 400,00 | 520,00 | 6,00 |
| >10≤16 | 340,00 | 520,00 | 7,00 |
| >16≤25 | 310,00 | 520,00 | 8,00 |
| >25≤40 | 265,00 | 460,00 | 9,00 |
| >40≤100 | 205,00 | 380,00 | 11,00 |
| >100 | 205,00 | 380,00 | 11,00 |
* Delivery condition: as rolled.
Semi-hard, tough carbon-steel, easily machinable by cold-strain.
Weldability:
Easily weldable.
Hardenability:
Extremely low hardenability, used above all for pieces of small section and when deformations due to water-quenching are allowed.
Notes:
CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):
| DIN 17200 |
| C22 |